"Her niche: unusual glass, clay and hand stitched beads she painstakingly makes from scratch"  ...  Essence Magazine

 

Watch YouTube How It's Made Interview:


​

fused glass bowl - 12" diameter

 

Covid-19 work precautions:

Dear Loved Customers, I hope you are all weathering this storm with big faith and are in good health.  

Please rest assured that any work I am doing, equipment, tools, boxes, packing supplies, are sanitized on a daily basis. Before shipping to you I will prep your purchase with either ultraviolet light or with disinfectant wipes.

I am and will continue safe distancing, hand washing and social isolation for as long as necessary.

​

​

​

about the artist

I've been designing jewelry for over 30 years. My education consists of glass, ceramics, beading and other classes I've taken at various art centers in Atlanta since 1988.  In 2020, the self-confinement resulting from COVID-19, has allowed me to explore my desire to combine my glass and ceramics into art other than jewelry which has been my concentration for the last 22 years. It has been challenging, but the forced isolation has allowed me time I have never had before to work out form and design. I am still in process. Always learning. Always transforming.

 

CERAMICS

Clay is shaped by hand into various shapes. Textures and designs are added. After air drying for several days, the beads are placed in the kiln to harden in a bisque firing.
After this, the pieces are painted with glazes and fired one or more times creating a permanent finish. Some beads are hand painted and decorated, then sealed.

RAKU is a special firing process which involves removing the beads from the kiln while they are molten hot and rushing them to a fireproof container filled with shredded newspaper or other flammable materials. The flame produced reacts with the oxygen in the air producing unique reactions with the glaze when the container is sealed. The resulting pieces have beautiful colors which cannot be duplicated.

​

FUSED GLASS

Very small pieces of glass are cut by hand from colored sheets. These pieces are arranged into several layers and lightly glued together. The completed designs are placed into a kiln and fired to high temperatures (1300-1550 degrees) where the layers melt (fuse) together permanently.

​

TORCH WORK GLASS BEADS

Rods of colored glass are melted around a steel mandrel using a torch. The glass softens around 1700 degrees and can then be manipulated. Decorative components such as gold and silver leaf or foil, dichroic glass, fine silver wire, enamel powders are added after the bead is shaped. The finished bead is placed in a kiln to "soak" at the annealing temperature for several hours to prevent breakage in the future.

​

I enjoy combining the elements of shiny smooth glass with matte textured clay into jewelry and art. It is challenging and rewarding to see "what will become".